BÖCK Silosysteme: Silage film Oasis

light green/black, oxygen barrier, UV-stabilized, 90 microns

Download printable version

The certification mark

The DLG QUALITY SEAL for operating equipment and con­sum­ables encompasses products, which are subjected to extensive testing of their value-determining and advertised characteristics. The tested criteria and the requirements to be fulfilled are spe­cified by independent commissions and are designed – over and above legal requirements – to prove the product’s fitness for purpose, its advertised characteristics and practical requirements. Testing contents and requirements are developed further by the responsible specialist departments of the DLG e.V. in line with the applicable legislation, as well as with technical and scientific progress. Successful testing is concluded with the assignment of the DLG QUALITY SEAL. The approved products are then published.

The DLG quality seal test included technical measurements in the laboratory. The test basis was the DLG test frame for for recyclate-free and recyclate-containing silage films made of low-density polyethylene (PE-LD) with and without barrier layers, as of November 2022.

Assessment in brief

The silage film Oasis, light green/black, UV-stabilized, 90 microns tested here, was tested in the DLG quality seal test in the laboratory on mechanical, physical, chemical and aging properties.

Table 1: Assessment in brief

DLG QUALITY PROFILERequirementEvaluation*
Film dimensions≥ nominal length, ≥ 98 % nominal width

Film thickness0,076 ≤ d ≤ 0,084 mm

Material conditionevenly coloured, free of streaks and pores

Tearing force in new conditionlongitudinally, transversely, over folds: ≥ 25 N/cm

Elongation of tears in new conditionlongitudinally, transversely, over folds: ≥ 400 %

Tear resistance in new statelongitudinally, transversely, over folds: ≥ 17 MPa

Dart drop resistance in new conditioncompliance with the manufacturer's declaration

Elongation of tear transversely after acid storagereduction: ≤ 15 %

Tear resistance transverse after acid storagereduction: < 10 %

Elongation of tears transversely after aging (weathering)> 350 %; reduction in new condition: < 30 %

Change in size after warm storage after aginglongitudinal: ≤ 2 % / transverse: < 2 %

Oxygen permeability in 0,2 bar< 250 cm³/(m² · d)

*    Evaluation range: requirements fulfilled () / requirements not fulfilled (X)

The Product

Description and Technical Data

Light green/black oxygen barrier silage film poly­ethylene (PE) and ethylene vinyl alcohol copolymer (EVOH), UV-stabilized, nominal thickness 90 microns.
The silage film Oasis is produced in rolls up to 4 meters wide and produced with high-frequency welding technology to the desired width. The rollers are fitted with a protective case combination wrapped in film with welded fleece. This is to avoid transport damage.

Table 2: Technical data (company information)

Main dimensions  
Nominal thickness 90 µm
Length 35, 50, 150, 200 m
Width up to 72 m

Individual widths and sizes available on request.

The Method


The suitability of the silo film was determined on the basis of the laboratory results judged.

Film dimensions

The length and width of the silo foil are calibrated band measurement.

Film thickness

The film thickness is calculated in accordance with DIN 53370:2006-11, method P at +23 °C (stay with regenerate film the stalks are not taken into account).

Material quality

It is visually checked whether the film has a evenly has opaque colouring and is free of smears and pores.


Important parameters for the strength of a silo film are tearing force (per cm film width), tear resistance (based on the cross-section of the sample body) and the elongation of the rip (elongation of the specimen to the breaking). Tear force, elongation and tear resistance longi­tu­dinal, transverse and over folds are measured in accordance to DIN according to DIN EN ISO 527-3:2003-07 at +23 °C; test speed 500 mm/min; Type 2 sample body; deformation measurement between measuring marks, in new condition measured by acid storage. Acid storage: 10 days storage in mixed acid from 3 % milk, 1.5 % vinegar, 0.5 % butyric acid.

The penetration resistance of the film is applied in surface, fold and the weld based on DIN EN ISO 7765-1:2004-10, procedure A performed. In doing
so, the values specified by the manufacturer are checked.

Aging behaviour/weather resistance

The weathering of the material is controlled with xenon arc lamps according to DIN EN ISO 4892-2, method A, synchronisation with irrigation 102/18 to 2000 MJ/m2, black standard temperature 60 ±3 °C, relative humidity 65 ±3 %, EUV=60 W/m2. After that, the elongation of the tear is 527-3:2003-07 measured in transverse direction.

Change in measure after hot storage

The dimensional measured is changed in accordance with DIN 53377:2007-10 Change in moderation after 1/2 hour storage in +80 °C hot air.

Gas permeability

The gas permeability is determined according to DIN 53380-3: 1998-07 with oxygen at +23 °C; 0.2 bar, investigated.

Continuous monitoring audit

The product quality is determined according to the annually by a DLG monitoring audit controlled. In addition, the manufacturer must measures of self-control in production obliged.

Detailed account of the test results


The silage film Oasis, light green/black, UV-stabilized, 90 microns, is suitable for silage cover.

Film dimensions

The measured film dimensions corresponded to film length and film width of the declaration.

Film thickness

As an average value for the film thickness, 0.090 mm was determined. The measured microvalue was 0.084 mm and the measured maximum value was 0.095 mm. As a result, the requirements for the mean for the film thickness and the permissible deviations are of the average value have been complied with.

Material quality

The film was uniformly opaquely coloured, free of streaks and pores.


In new condition

The tearing force was 31.3 N/cm, transverse 32.0 N/cm and over folds 30.9 N/cm (minimum value 25 N/cm each). Taking into account the film thickness resulting in a tear resistance longitudinally of 35.8 MPa , across 36.0 MPa and over folds 34.7 MPa (minimum value 17 MPa each). The elongation at the break was 635 %, transver­sely 647 % and over folds at 636 % above the required minimum value of 400 %. The film thus fulfilled the requirements.

After acid storage
After ten days of storage in a mixed acid (3 % milk, 1.5 % vinegar and 0.5 % butyric acid) reduction in tear resistance transversely was 2.3 % (permissible ≤ 10 %); the reduction of the elongation of the transversely was 0.6 % (allowed ≤ 15 %). Acid resistance was thus given.

Dart drop resistance

When checking the penetration resistance in the surface, fold and weld are Manufacturer specified values area ≥ 650 g, fold ≥ 450 g and weld ≥ 650 g.

Aging behaviour/weather resistance

After simulation of a one-year natural outdoor ­weathering with 2000 MJ/m2, the elongation of the 558 % (minimum value 350 %), i.e. equivalent to a reduction in elongation of 13.8 % (permissible 30 %) related to the new state. Weather resistance was
thus given.

Change in measure after hot storage

The dimensional changes after hot storage at 80 °C of warm air was longitudinally at -0.1 % and transversely 0.1 % below the permitted limit of ≤ 2 %.
The temperature resistance was thus given.

Gas permeability

Oxygen permeability at 0.2 bar was film with 0.62 cm³/(m² · d) lower than the maximum permissible value 250 cm³/(m² · d).


The criteria tested in this DLG quality seal test are evaluated on the basis of laboratory tests the mechanical, physical, chemical and aging properties of the Oasis silage film, light green/black, UV-stabilized, 90 microns. The tested silage film Oasis, light green/black, UV-stabilized, 90 microns, has met the requirements of the test frame with regard to the criteria examined.

Applicant and test implementation


BÖCK Silosysteme GmbH,
Stefan-Flötzl-Straße 24,
D-83342 Tacherting

Phone: +49 (0) 8621 6466-0,
Fax +49 (0) 8621 6466-46

Test implementation

DLG TestService GmbH, Gross-Umstadt location
The tests are conducted on behalf of DLG e.V.

DLG test framework
DLG quality seal test "for recyclate-free and recyclate-containing silage films made of low-density polyethylene (PE-LD) with and without barrier layers", (current as of 11/2022)

Farm input

Head of Department
Dr. Michael Eise

Test engineer(s)
Dr. Harald Reubold *

SKZ-Testing GmbH, Friedrich-Bergius-Ring 22, 97076 Würzburg
Kunststoff-Zentrum in Leipzig GmbH, Erich-Zeigner-Allee 44, 04229 Leipzig

DLG Test commission
Stefan Wolf, 63110 Rodgau Weiskirchen
Christof Löffler, LAZBW Aulendorf, 88326 Aulendorf
Karsten Bommelmann, AG FUKO, 26160 Bad Zwischenahn
Willi Schüler, 64395 Brensbach Wallbach
Dr. Klaus Hünting, VBZL Haus Riswick, 47533 Kleve
Dipl.-Ing. Udo Dengel, SKZ-Testing GmbH, 97076 Würzburg

* Author